牌号简介 About |
---|
Veradel® LTG-3301聚醚砜(PESU)能够直接金属化高质量反射表面,适用于需要高热变形、良好韧性和尺寸稳定性的应用。其他理想的性能包括热稳定性、抗蠕变和低吸湿性。注射成型时,树脂表现出良好的流动性。潜在的应用包括汽车前照灯反射镜、雾灯反射镜、驻车和转向反射镜,以及其他需要直接金属化的优良表面光洁度的应用。Veradel® LTG-3301树脂有多种颜色可供选择。Veradel LTG-3000 BK 184 MR(黑色)Veradel® LTG-3301 NT MR(天然) Veradel® LTG-3301 polyethersulfone (PESU) offers the ability to directly metalize high-quality reflective surfaces for applications that require high heat deflection, excellent toughness and dimensional stability. Other desirable properties include thermal stability, creep resistance, and low moisture absorption. The resin exhibits superior flow when injection molded. Potential applications include automotive headlamp reflectors, fog lamp reflectors, park and turn reflectors, and other applications where excellent surface finish for direct metallization is desired. Veradel® LTG-3301 resin is available in a variety of colors. Veradel® LTG-3000 BK 184 MR (black) Veradel® LTG-3301 NT MR (natural) Veradel® A-301 BG 903 MR (beige) Veradel® LTG-3000 GY 001 MR (gray) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.37 | g/cm³ | ASTM D792 |
23℃ 23℃ |
1.37 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
380℃,2.16kg 380℃,2.16kg |
30 | g/10min | ASTM D1238,ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.54 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
23℃,4 mm 23℃,4 mm 2 |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃,4.00 mm Yield, 23 ℃, 4.00 mm 3 |
MPa | ISO 527 | |
-- -- |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield 3 |
% | ISO 527 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790,ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
J/m | ASTM D256 | |
-- -- |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180 | ||
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,退火,4.0 mm 1.8 MPa, annealed, 4.0 mm 4 |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 5 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
相对温度指数 Relative temperature index |
|||
电气性能,0.79 mm Electrical performance, 0.79 mm |
℃ | UL 746 | |
冲击机械性能,1.60 mm Impact mechanical performance, 1.60 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 |
备注 |
---|
2 1 mm/min |
3 50 mm/min |
4 annealed 1 hour at 200°C |
5 50°C/h, A (10N) |
【新闻资讯】查看全部
神马股份拟收购尼龙化工37.72%股权延伸产业链,角逐市场龙头
2019-10-14 神马股份10月11日晚间公告,拟通过发行股份及支付现金,购买控股股东中国平煤神马集团持有的尼龙化工公司37.72%股权。同时,公司拟募集配套资金。本次交易完成后,上市公司将控股 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |