b 4米兰诺是一种挤出级,特别适用于美学应用。它结合了热特性和流变特性,使得大尺寸的片材也能挤出,具有良好的表面光洁度(极低的凝胶含量)。名称:热塑性ISO 2580-ABS 1,EGN,105-04-16-20应用特殊等级,用于实现需要典型ABS特性的美学产品。 B 4 Milano is an extrusion grade specially suitable in aesthetics applications. It combines thermal characteristics and rheological properties which allow the extrusion of sheets also of large size with an excellent surface finishing (very low gels content). Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 Applications Special grade for the realization of aesthetics goods that need typical ABS characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
220℃,10.0kg 220℃,10.0kg |
4.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.40 到 0.60 | % | 内部方法 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
12 | kJ/m² | DIN 53453 |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
DIN 53453 | ||
-40℃ -40℃ |
DIN 53453 | ||
23℃ 23℃ |
DIN 53453 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃,3.2mm -40℃,3.2mm |
J/m | ISO 180-4A | |
-20℃,3.2mm -20℃,3.2mm |
J/m | ISO 180-4A | |
0℃,3.2mm 0℃,3.2mm |
J/m | ISO 180-4A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ISO 180-4A | |
-40℃ -40℃ 4 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 4 |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ISO 306/A120 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Designation Designation |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
拉伸强度 tensile strength 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 |
备注 |
---|
2 50 mm/min |
3 2.0 mm/min |
4 4 mm |
【新闻资讯】查看全部
扬子石化乙烯日产2390吨创出新纪录
2018-02-02 扬子石化烯烃厂通过优化裂解炉运行组合、提高优质原料投入比例、提高裂解系统运行效率,乙烯日产长时期保持在2300吨高负荷,1月24日单日产量达到2390吨,创出了乙烯装置自运行以来最高日产新记录。 2017年以来,全球乙烯价格坚挺,并长时间保持在10000元/吨的历史高位,乙烯单体成为石化行业经济附加值最高的产品,并与部分下游产品呈价格倒挂之势。 扬子石化抓住市场机遇,确立了乙烯产量最大化运营策略,围绕增产乙烯开展运行装置优化组合。2017年11月、12月两个 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |