牌号简介 About |
---|
Riblene® FC 39 D是一种高分子量低密度聚乙烯(LDPE),适用于吹塑薄膜挤出。Riblene® FC 39 D的特点是具有较高的熔融强度,在挤压过程中具有良好的气泡稳定性。由Riblene® FC 39 D制造的薄膜容易热收缩,具有高硬度、良好的机械和光学性能。主要应用Riblene® FC 39 D推荐用于生产中等硬度的收缩膜,具有良好的清晰度和光泽。 Riblene FC 39 D is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 39 D is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 39 D are easily heat shrinkable and characterised by high rigidity, good mechanical and optical properties. Main Application Riblene FC 39 D is recommended for the production of medium rigidity shrink film characterized by good clarity and gloss. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
70 | µm | |
薄膜厚度 film thickness |
40 to 150 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,70 µm,吹塑薄膜 1% secant, MD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,70 µm,吹塑薄膜 1% secant, TD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,70 µm,吹塑薄膜 MD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,70 µm,吹塑薄膜 TD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
70 µm,吹塑薄膜 70 µ m, blow molded film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD:70.0 µm MD:70.0 µm |
kN/m | ISO 6383-2 | |
TD:70.0 µm TD:70.0 µm |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,70 µm,吹塑薄膜 45 °, 70 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
70.0 µm,吹塑薄膜 70.0 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
制止在海南岛内消费 一次性塑料制品
2016-01-28 海南省7年多前就限制生产、运输、销售、储存、使用一次性塑料制品,也取得一定成效,但目前在城市、农村、旅游景点、海边、田间地头等,仍可看到大量丢弃的一次性塑料制品。王光业等代表建议加大宣传力度,严禁在岛内生产一次性塑料制品,加大对进岛一次性塑料制品的查处力度,加强回收利用,推广环保替代品。 王光业代表说,导致目前海南一次性塑料制品屡禁不止的原因主要有四个,一是民众环保意识不强,生活习惯难以改变;二是流通渠道多,监管难度大;三是替代品跟不上,农贸市场大多因为合格袋价格过高而不愿 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |