BMC 605L成型化合物是一种低成本的矿物填充玻璃纤维增强聚酯化合物,适用于压缩、转移和填充器注射成型。具有良好的成型性、中等的冲击强度、优良的综合电气性能和阻燃性。典型应用包括断路器、变压器线轴和电机端盖。BMC 605L模塑料是在工业颜色范围内以挤压形式生产的。它有12英寸长的原木或特定重量的预切段塞,直径为1“至2½”。在这个范围内,较小的直径作为多个挤压件提供,重量公差为正负5%,最大为正负15克。 BMC 605L molding compound is a low cost, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is characterized by good moldability, medium impact strength, excellent overall electrical properties and flame resistance. Typical applications include circuit breakers, transformer bobbins and motor end bells. BMC 605L molding compound is produced in extruded form in a range on industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters 1" to 2 ½" . Within this range, smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5 %, up to a maximum of plus or minus 15 grams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.95 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.25 to 0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.14 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
110 to 320 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
巴氏硬度 Babbitt hardness 2 |
ASTM D2583 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
PC、PMMA价钱齐下跌
2017-10-10 总行情:节后首个工作日,中国塑料城工程塑料市场报盘多维持节前价位,个别走高。场内业者多观望为主,下游观望氛围较浓,交投暂时有限。 预计,今日市场基本面不会出现太大调 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |