牌号简介 About |
---|
在复杂金属有机催化剂存在下乙烯气相聚合得到的产物。稳定配方:抗酸剂、抗氧化剂、热稳定剂、加工助剂、分散剂。用途:用于薄膜袋的高强度吹塑薄膜。技术要求:TU 2211-145-05766801-2008 Product obtained by gas phase polymerization of ethylene with hexane-1 in presence of complex metalorganic catalysts. Stabilization recipe: antacid, heat stabilizer, processing additive, dispersant. Application: high-strength tubular film for the production of thin bags |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.946 到 0.950 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,5.0kg 190℃,5.0kg |
0.25 到 0.40 | g/10min | ASTM D1238 |
凝胶含量 Gel content 2 |
600 | pcs/m² | |
熔体流比 Melt flow ratio |
|||
MFR 21.6 kg/MFR 5.0 kg MFR 21.6 kg/MFR 5.0 kg |
> 18.0 | ASTM D1238 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD 2% secant, MD |
700 | MPa | ASTM D882 |
2% 正割,TD 2% secant, TD |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 p.6 Attachment A TU 2211-14505766801 |
【新闻资讯】查看全部
国内首套自主开发PO/TBA技术工业化试验圆满完成!
2020-12-22 搜料网资讯: 经过72小时稳定运行 12月17日23点10分 伴随最后一个样品分析结果的全面达标 标志着滨化集团PO/TBA工业化试验取得圆满成功 这是国内首个具有自主知识产权的PO/TBA技术 对于 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |