牌号简介 About |
---|
采用CSTR浆体工艺技术,生产出5000支篷布用扁纱。5000s非常适合用于单丝应用。5000S具有良好的拉伸、旋压、高强度和熔融稳定性。 5000S is manufactured to be processed in flat yarn for tarpaulin by CSTR Slurry process technology. 5000S is ideally suited for use in monofilament application. 5000S offers good stretching, spinning, high strength property and melting stability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.954 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.95 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
200 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
74.0 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
125 | ℃ | ASTM D1525 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
探讨聚氨酯保温资料行业开展趋势
2016-11-24 在近日举行的中国国际新材料展览会上,聚氨酯保温材料企业及制备设备企业占了半壁江山。一位聚氨酯保温材料企业负责人告诉记者:“今年聚氨酯保温材料的消耗量明显增长,在国家大力推动绿色节能建筑建设的背景下,聚氨酯保温材料的发展前景十分广阔。” 建筑用硬泡聚氨酯保温材料传热系数为0.017-0.024,与其他保温材料相比,传热系数最低,保温性能最好。而且,经过改良的聚氨酯材料低烟、低毒,不污染环境,即使发生火灾,也因其有高效碳化层保护而对环境起到保护作用。不仅如此,聚氨酯材料具有牢固 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |