牌号简介 About |
---|
聚酰胺6玻璃纤维增强25%,UL94V0自熄,阻燃性好,厚度低,流动性好,力学性能好。UL94 V0批准所有颜色为0.97 mm。UL746B已批准。可供选择:不同颜色,热稳定(H),释放剂(W),不含PBDE/PBDF。 Polyamide 6 glass fiber reinforced 25%, UL94 V0 self extinguishing, good flame proofing also at low thickness, good flow and good mechanical properties. UL94 V0 approuved all colors at 0,97 mm. UL746B approved. Available: different colors, heat stabilized (H), release agent (W), and without PBDE/PBDF. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 到 1.32 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
12 | g/10min | ASTM D1238,ISO 1133 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
0.30 到 0.40 | % | |
TD TD |
0.60 到 0.80 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.0 | % | ASTM D570,ISO 62 |
饱和 saturated |
% | ASTM D570 | |
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
Granule Humidity Granule Humidity |
% | 内部方法 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 1 |
|||
23℃ 23℃ 1 |
kJ/m² | ASTM D256,ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ISO 180,ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648,ISO 75-2/A | |
连续使用温度 Continuous use temperature |
IEC 60216 | ||
-- -- 2 |
℃ | ||
-- -- 3 |
℃ | ||
-- -- 4 |
℃ | ||
-- -- 5 |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306/B50, ASTM D1525 6 | |
熔融温度 Melting temperature |
℃ | ASTM D211,ISO 121 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638, ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638, ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638, ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790, ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ISO 178 | |
断裂 fracture |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6x4x50 mm |
3 20000 hrs |
4 Heat Stabilized, 20000 hrs |
5 Short Term |
6 Heat Stabilized, Short Term |
7 速率 A (50°C/h), 压 力1 (10N) |
8 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
巴西化肥进口量创纪录
2021-12-12 搜料网资讯: 近日,巴西国家商品供应公司(Conab)发布预测,2021/2022财年(2021年4月至2022年3月),得益于农作物面积的增加和良好的气候条件,巴西谷物产量有望达2.881亿吨,同比增长14. |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |