牌号简介 About |
---|
Ebarta AH 100是一种非常薄的未填充环氧树脂,可与不同的硬化剂一起使用。根据应用情况,合适的硬化剂可与树脂AH 100混合。快速硬化剂TGS用于薄层压板和小体积回填料。用于填充物性能的薄壁层压板小体积回填料粘合树脂未填充快速固化 ebalta AH 100 is a very thin, unfilled epoxy resin, which can be used with different hardeners. Depending on the application the suitable hardener can be mixed with the resin AH 100. The fast hardener TGS is used for thin laminates and small-volume back fillings. Applications Thin-walled laminates Low volume backfillings Bonding resin for fillers Properties unfilled fast curing |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
26 到 42 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.10 到 1.14 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
0.65 到 0.85 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
8.0 到 10 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
25 到 35 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Martens Temperature Martens Temperature |
℃ | DIN 53458 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【新闻资讯】查看全部
生物可降解塑料不是处置环境危害的出路
2017-08-03 “生物可降解塑料”因字面意思而被误认为这些塑料最终可在环境中降解、绿色无害,故人们丢弃这种塑料时心理负担不大。 然而,事实与人们的想法恰恰相反。生物可降解塑料不会在自然环境中降解,它会对环境、尤其是海洋环境造成持久污染。故被贴上“生物可降解”标签的产品的广泛使用并不会显著减少进入到海洋中的垃圾量,或者降低塑料对海洋环境所带来的物理和化学风险。 生物可降解塑料听起来是个很好的主意,但问题的关键是这些塑料事实上并非可以简单地通过生物途径降解。很多被称为生物可降解 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |