牌号简介 About |
---|
Shin Etsu Keg2000-40是一种快速固化型液体注射成型硅胶。它作为两种成分提供,以1:1的比例混合,以确保轻松和准确的混合。KEG2000-40的粘度很低,可以很容易地泵送到大多数注塑系统中。高温下高撕裂强度快速固化时间室温下长使用寿命典型应用O形圈隔膜盖橡胶辊连接器包装其他电气零件六级认证 Shin-Etsu KEG2000-40 is a fast cure type liquid injection molding silicone. It is supplied as two components which are mixed in a 1:1 ratio to ensure easy and accurate blending. The viscosity of KEG2000-40 is low enough to allow easy pumping through most injection molding systems. High tear strength Rapid cure time at elevated temperature Long pot life at room temperature Typical Applications O-Rings Diaphragms Capping Rubber Rollers Connector packaging Other electrical parts ClassVI certification |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
41 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
9.60 | MPa | |
100% 应变 100% strain |
1.23 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
640 | % | |
撕裂强度 tear strength 2 |
kN/m | ||
压缩形变 Compression deformation |
|||
180℃,22 hr 180℃,22 hr |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
|||
32℃ 32℃ |
wk | ||
后固化时间 Post curing time |
|||
200℃ 200℃ |
hr | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 模具 |
【新闻资讯】查看全部
2400亿卢布!印度石油将在古吉拉特邦炼油厂建立新的石化项目
2021-06-10 搜料网资讯: 印度石油公司(IOC)6月7日晚间表示,公司已与古吉拉特邦政府签署协议,将投资约2400亿卢布(33亿美元),在位于瓦达多拉的印度石油公司炼油厂建立新的石化项目。 印 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |