牌号简介 About |
---|
低密度湿固化聚乙烯,用于低压建筑电线应用(UL型XHW-2、RHW-2、RHH、SIS、USE-2-UL‘防晒’)Pexidan® X/T-UV是一种低密度交联聚乙烯系统,可湿固化,由硅烷预接枝碱化合物A-3001和阻燃催化剂母粒CAT-005FRUv1组成。以适当的比例(80:20)混合和挤压,这两种成分形成一种材料,该材料可通过暴露于70-90°C热水或甚至环境湿度进行固化。Pexidan® X/T-UV是符合RoHS的系统。根据UL44,使用该系统制造的绝缘材料可标记为所有颜色的SUNRES,尺寸为6 AWG及以上。 Low density moisture curable polyethylene for low voltage building wire applications (UL styles XHHW-2, RHW-2, RHH, SIS, USE-2 - UL ‘SUNRES') PEXIDAN® X/T-UV is a low density flame-retardant XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-005FR-UV1. Mixed and extruded in the proper proportions (80:20), the two components result in a material that is curable by exposure to 70-95°C hot water or even ambient moisture. PEXIDAN® X/T-UV is halogenated but is RoHS-compliant. Insulation may be marked SUNRES or SR in all colors for sizes of 6 AWG and larger per UL44. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.02 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
67 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
UL 1581 | ||
屈服 yield |
12.4 | MPa | UL 1581 |
断裂 fracture |
16.2 | MPa | UL 1581 |
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | UL 1581 | |
断裂 fracture 4 |
MPa | UL 1581 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | UL 1581 | |
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | UL 1581 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
老化测试 Aging test |
UL 1581 | ||
Elongation after exposure Elongation after exposure 5 |
% | UL 1581 | |
Elongation after exposure Elongation after exposure 6 |
% | UL 1581 | |
Original elongation Original elongation |
% | UL 1581 | |
Original tensile strength Original tensile strength |
MPa | UL 1581 | |
曝光后拉伸强度 Tensile strength after exposure 5 |
MPa | UL 1581 | |
曝光后拉伸强度 Tensile strength after exposure 6 |
MPa | UL 1581 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
变形 deformation |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
90 ℃,60 Hz 90 ℃,60 Hz |
UL 1581 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
击穿电压 breakdown voltage |
UL 1581 | ||
-- -- |
V | UL 1581 | |
after glancing impact after glancing impact |
V | UL 1581 | |
绝缘电阻 insulation resistance |
UL 1581 | ||
23℃ 23℃ |
Mohms/1000 ft | UL 1581 | |
90℃ 90℃ |
Mohms/1000 ft | UL 1581 | |
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/1000 ft | UL 1581 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
|||
4.0 mm 4.0 mm |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
酸性气体排放 Acid gas emissions |
|||
HBr HBr |
% | CSA C22.2 No. 0.3 Method 2 | |
Crushing Test Crushing Test |
g | UL 1581 | |
高温伸长率 High temperature elongation 7 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 7 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 After 60 day oil @ 75°C |
3 After 30 day gasoline @ 23°C |
4 After thermal ageing (7days @121°C) |
5 300 hr. exposure |
6 720 hr. exposure - SUNRES |
7 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
日本正协作推进汽车零配件向轻量化演进的研发活动
2018-08-31 新材料正在改变汽车的未来。日本正合作推进车体、轮胎、车窗等主要汽车零配件向轻量化演进的研发活动。这其中的关键是能够让塑料成为可用之材的高分子化合物。研发活动的既定目标是将现有汽车车身重量减少半,新材料的使用将有望助力电动 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |