Greenflex® FF 35是用于吹塑薄膜挤出的乙烯-醋酸乙烯共聚物(EVA)。该树脂具有良好的拉伸性和密封性。主要用途Greenflex® FF 35适用于具有良好断裂力学性能的软包装薄膜,用于拉伸罩包装和型材挤压。 Greenflex FF 35 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. The resin shows good stretchability and sealability. Main Application Greenflex FF 35 is suitable for flexible packaging film having good fracture mechanical properties, for stretch hood packaging and profiles extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.929 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ISO 1133 |
醋酸乙烯含量 Vinyl acetate content |
9.0 | wt% | Internal Method |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
94 | ISO 868 | |
邵氏 D,注塑成型 Shaw's D, injection molding |
42 | ISO 868 | |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
ISO 8295 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,吹塑薄膜 1% secant, MD, blow molded film |
MPa | ISO 527-3 | |
1% 正割,TD,吹塑薄膜 1% secant, TD, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
% | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
吹塑薄膜 Blown film 2 |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 3 |
ISO 6383-2 | ||
MD MD |
kN/m | ISO 6383-2 | |
TD TD |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
吹塑薄膜 Blown film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 Blown Film |
【新闻资讯】查看全部
纽约著名栈道以塑料聚合物替代木材重建
2016-01-22 纽约市标志性的2.7英里Coney Island栈道正在进入重建一期阶段。 长时间的使用和超级风暴桑迪的侵袭使这条著名的栈道老旧不堪。但有人认为,用混凝土和再生塑料取代木板的计划将最终毁灭这一标志性目的地。 位于美国伊利诺伊州Aurora的Tangent Technologies LLC公司用回收的牛奶壶和洗涤剂瓶制成的高密度聚乙烯板材不久将被铺设到混凝土结构上方,构筑栈道。 据纽约市公园与娱乐管理局介绍,在耗资690万美元的重建初步阶段,人 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |