牌号简介 About |
---|
聚酰胺6.6,黑色,25%玻璃纤维增强,抗水解和紫外线。良好的热性能,电气和机械性能。非常适合注塑成型。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.49 | g/cm³ | ASTM D792 |
密度 Density |
1.53 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
0.70 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
0.20 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.66 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
摩擦系数 friction coefficient |
ASTM D3702 Modified | ||
动态 dynamic |
ASTM D3702 Modified | ||
静态 static state |
ASTM D3702 Modified | ||
磨损因数 Wear factor |
|||
Washer Washer |
10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 3 |
|||
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2017年中国化工专利奖揭晓
2017-12-26 日前,2017年度中国化工专利奖名单揭晓。全系统共有42项专利和24家企业获表彰。本届获奖专利数和企业数为历年最多。 近年来,集团公司专利申请逐年增加、专利申报质量明显改善、专利布局逐渐全球化、国际化、企业专利管理逐步显现专业水平,很好地展示了企业在创造质量高、运用效益好、保护能力强、管理水平高的专利项目上取得的进步。 今年获奖的专利和企业是经过项目申报、专业公司初评和行业专家函审等程序,并最终由专家组会审而产生的。“带两个顺放罐的变压吸附工艺”等42项专利 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |