牌号简介 About |
---|
PRL PPX-EN-FR3是一种聚苯醚 + PS (PPE+PS)产品,。 它可以通过挤出进行加工,在北美洲有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 Flame Retardant 无卤素 耐热 PRL PPX-EN-FR3 is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by extrusion and is available in North America. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Halogen Free Heat Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,11.6kg 250℃,11.6kg |
4.0 to 8.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃,3.2mm -40℃,3.2mm |
130 | J/m | ASTM D256 |
23℃,3.2mm 23℃,3.2mm |
210 | J/m | ASTM D256 |
落锤冲击 Drop hammer impact |
|||
3.2 mm 3.2 mm |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.7 mm 1.7 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
1.7 mm 1.7 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | ASTM D149 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
0.750 mm 0.750 mm |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
1.7 mm 1.7 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率(HVTR)(0.750 mm) High voltage arc marking rate (HVTR) (0.750 mm) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
1.7 mm 1.7 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm,黑色 0.75 mm, black |
UL 94 | ||
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
1.70 mm,所有颜色 1.70 mm, all colors |
UL 94 | ||
3.00 mm,所有颜色 3.00 mm, all colors |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
帝斯曼于密歇根州设立研发中心
2016-09-27 荷兰皇家帝斯曼集团耗资五百万美元,于美国密歇根州特洛伊市新建了一所研发中心。此举旨在提高集团工程塑料制品方面的研发应用能力,并进一步扩大其在北美地区的影响力。 研发中心设备齐全、技术先进,可运用包括显微技术在内的多种手段对材料特性进行细致分析。此外,材料老化测试、耐化学性测试,以及包括流变学特性分析和热分析在内的多种测试亦不在话下。同时,中心对于3D打印的运用,也让快速成型技术成为了可能。 中心还设有专项实验室,主要负责同客户一起解决产品在特定条件下的实际运 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |