牌号简介 About |
---|
SABIC® LDPE 2308N0是不含添加剂的低密度聚乙烯管级。SABIC® LDPE 2308N0采用SABIC清洁管式反应器(CTR)技术生产,确保产品纯度高。它具有高韧性、良好的柔韧性和合理的抗环境应力开裂性,因此通常用于柔韧性和坚硬物品。应用注射成型:SABIC® LDPE 2308N0通常适用于注射成型应用,常用于盖和封口。母料配制:SABIC® LDPE 2308N0通常用作母料和配制应用的载体树脂。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LDPE 2308N0 is a LDPE tubular grade without additives. SABIC® LDPE 2308N0 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application Injection Molding: SABIC® LDPE 2308N0 is typically suitable for injection moulding application, frequently used for Caps & closures. Masterbatch Compounding: SABIC® LDPE 2308N0 is typically suitable as carrier resin for masterbatch and compounding applications. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
7.5 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
25 | g/10min | |
熔体体积流动速率 Melt Volume Rate |
ISO 1133 | ||
190℃,2.16 kg 190℃,2.16 kg |
10.0 | cm³/10min | |
190℃,5 kg 190℃,5 kg |
33.0 | cm³/10min | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ||
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | DIN 53765 | |
Enthalpy Change Enthalpy Change |
J/g | DIN 53765 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
MPa | ISO 527-2/1A/50 | |
拉伸强度 tensile strength |
ISO 527-2/1A/50 | ||
屈服,注塑成型 Yield, injection molding |
MPa | ||
断裂,注塑成型 Fracture, injection molding |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,注塑成型 Fracture, injection molding |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
煤化工与石化聚烯烃产品晋级,需关注车用塑料市场
2016-12-23 改性塑料是以通用塑料和工程塑料为基础,经过添加改性剂,和填充、共混、增强等加工方法,提升了阻燃性、强度、抗冲击性和韧性的塑料制品。改性塑料因其具有其他材料所不具备的特性而被汽车工业大量采用。随着汽车轻量化、节能环保的要求的日益提高,汽车改性塑料的用量逐年增加。 2016年10月,中国汽车工程学会发布《节能与新能源汽车技术路线图》。路线图指出,到2020年、2025年、2030年,整车质量需比2015年分别减重10%、20%、35%。汽车用工程塑料主要有聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |