牌号简介 About |
---|
Taitalac® 3000H是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在亚太地区或北美洲有供货,加工方式为:挤出或管路挤出成型。 Taitalac® 3000H的主要特性有: 阻燃/额定火焰 坚硬 耐化学品 高强度 Taitalac® 3000H的典型应用领域为:水管/管道/饮用水 Taitalac® 3000H is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for extrusion or pipe extrusion. Important attributes of Taitalac® 3000H are: Flame Rated Chemical Resistant High Strength Rigid Typical application of Taitalac® 3000H: Plumbing/Piping/Potable Water |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
200℃,5.0kg 200℃,5.0kg |
0.50 | g/10min | ASTM D1238 |
220℃,10.0kg 220℃,10.0kg |
5.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,12.7mm 23℃,12.7mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,12.7 mm 1.8 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,23℃,3.18 mm Fracture, 23 ℃, 3.18 mm 2 |
MPa | ASTM D638 | |
屈服,23℃,3.18 mm Yield, 23 ℃, 3.18 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃,3.18 mm Fracture, 23 ℃, 3.18 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,23℃ Yield, 23 ℃ 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.11 in/min |
4 压 力1 (10N) |
【新闻资讯】查看全部
废旧塑料加工成高档装饰板材
2016-04-08 按照规划,庄河今年将续建、新建千万元项目100多个,其中新开工项目40个以上。记者近日在庄河采访了解到,这些新推进的大项目都在瞄准资源消耗低、绿色增长这个新目标。 近日,大连昌泰建筑模板新材料项目签约落户大连新兴产业经济区。这一项目总投资1亿1千万元,采用资源再生利用新技术,将农作物秸秆、谷壳和废旧塑料加工成高档装饰板材,进一步完善园区循环经济产业链条。 柳永海 大连昌泰科技开发有限公司总经理:市场调研已经在招商局(帮助下)调研到位了,庄河大的家具厂我们可以 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |