牌号简介 About |
---|
LLHF-117XA是一种经认证的优质乙烯-己烯共聚物,专门为超强度吹塑薄膜的突出冲击和韧性而开发。LLHF-117XA具有良好的加工性能,薄膜具有优异的Elmendorf撕裂强度和抗穿刺性能。LLHF-117XA的主要应用包括超强衬里、层压膜、拉伸包装膜和超强手提袋。建议的最大薄膜降深为0.3 mil。LLHF-117XA不含防滑块。LLHF-117XA符合FDA法规21CFR 177.1520(c)3.2(a)和大多数与食品接触的聚乙烯使用相关的国际法规。 LLHF-117XA is a certified prime grade Ethylene-Hexene Copolymer specially developed for extrusion of SUPER STRENGTH Blown films of outstanding Impact and Toughness. LLHF-117XA features good processability and films exhibit exceptional Elmendorf Tear strength and Puncture resistance. LLHF-117XA major applications include super strong liners, lamination films, stretch wrapping films, and super strong carry-on-bags. Maximum recommended film drawdown is 0.3 mil. LLHF-117XA contains no slip and no antiblock. LLHF-117XA complies with FDA regulation 21CFR 177.1520 (c) 3.2(a) and most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,25 µm 1% secant, TD, 25 µ m |
207 | MPa | ASTM D882 |
1% 正割,MD,25 µm 1% secant, MD, 25 µ m |
193 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm TD, fracture, 25 µ m |
MPa | ASTM D882 | |
TD,屈服,25 µm TD, yield, 25 µ m |
MPa | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ASTM D882 | |
MD,屈服,25 µm MD, yield, 25 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm 25 µm 2 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,25 µm MD,25 µm |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD,25 µm TD,25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
常温可降解!韩国亚洲大学成功开发出了一种新的PBAT材料
2022-11-18 扫描上图二维码,可以免费下载 搜料 APP 近日, 韩国亚洲 大学李分烈教授、李平天教授团队成功 开发出了一种新的PBAT材料,可以在25摄氏度下降解。 科研团队将磷酸金属盐作为催化剂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |