牌号简介 About |
---|
VERSIFY™ 2300 弹性体为吹塑拉伸套罩薄膜带来优化的平衡性能,这种薄膜旨在确保托盘货物在储存和运输过程中的完整性。该产品具有优异的弹性,与其他产品相比,它具有相同的或者是更佳的固定能力。这种薄膜可提高托盘货物的稳定性,具有更佳的抗撕裂性能,易于回收利用和处置。该牌号特别适宜于多种流延和挤出加工,也可作为共混组分用于热塑性弹性体。 VERSIFY™ 2300 Elastomer generates the optimum performance balance for blown stretch hoods - the wrapping that ensures the integrity of goods pallets being stored and transported. It provides excellent elasticity and good holding force at equal or better cost than competitor solutions. The film improves pallet stability, delivers better tear resistance and makes recycling and disposal much simpler. The grade is also ideally suited to a range of calendering and extruded applications and as a blend component for thermoplastic elastomers. Complies with: U.S. FDA FCN 909 U.S. FDA 21 CFR 175.105(c)(5) EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.867 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
总结晶性 Summary of crystallinity |
13 | % | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
-27.0 | ℃ | 内部方法 |
维卡软化温度 Vicat Softening Temp |
43.0 | ℃ | ASTM D1525 |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D523 | ||
20°,1000 µm,模压成型 20 °, 1000 µ m, molded |
ASTM D523 | ||
60°,1000 µm,模压成型 60 °, 1000 µ m, molded |
ASTM D523 | ||
雾度 Haze |
|||
2000 µm,注塑成型 2000 µ m, injection molding |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
ASTM D2240 | ||
邵氏 A,模压成型 Shaw A, molded |
ASTM D2240 | ||
邵氏 D,模压成型 Shaw's D, molded |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂,模压成型 Fracture, molded 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D790 |
备注 |
---|
1 Brominated |
2 一般属性:这些不能被视为规格。 |
3 Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
【新闻资讯】查看全部
五月聚乙烯全线飘红可能性分析
2022-05-11 国际油价不断攀升以及部分石化装置检修,是支撑行情的主要动力,但终端及期货配合欠佳,高价货源成交不畅,则抑制了市场继续向好的空间,起伏的走势为后市平添了许多不确定性 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |