牌号简介 About |
---|
M21G764特别适用于单挤压和共挤压应用,如深度冷冻、一般的填表密封膜和薄袋。在共混物和共挤出物中,它们可用于提高LLDPE、LDPE和再生聚乙烯的冲击强度。M21G764是通过乙烯-甲基丙烯酸共聚物的中和作用产生的离聚物。M21G764仅包含反块。它们具有以下特性:在环境和低温下具有很高的冲击强度。如果需要较低的滑动水平或仅用于低滑动膜,可以添加M 21 G 764例外的下降。添加其他聚合物、母料和颜料,或使用其他厚度可能会改变薄膜滑动和防阻塞性能。如果需要电晕处理,水平通常应在38-48mn/m范围内。我们建议您咨询您的INEOS技术代表,以获得关于M21G764使用的进一步建议。 M21G764 are particularly suitable for mono and co-extrusion applications such as deep freeze, form fill seal film in general and thin bags. In blends and co-extrusions, they can be used to boost the impact strength of LLDPE, LDPE and recycled polyethylene. M21G764 are ionomers, produced by neutralisation of an ethylene - methacrylic acid copolymer. M21G764 contains only antiblock. They offer the following properties: Very high impact strength at ambient and low temperatures Exceptional drawdown M 21 G 764 can be added if a lower slip level is required or used pure for low slip films. Addition of other polymers, masterbatches and pigments, or use of other thicknesses may alter film slip and antiblock performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS technical representative for further advice on the use of M21G764. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,0.325kg 190℃,0.325kg |
0.95 | g/10min | ISO 1133 |
Methacrylic Acid Content Methacrylic Acid Content |
1.0 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
> 0.50 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
拉伸模量 Tensile modulus |
|||
1% 正割,MD,50 µm,吹塑薄膜 1% secant, MD, 50 µ m, blow molded film |
MPa | ||
1% 正割,TD,50 µm,吹塑薄膜 1% secant, TD, 50 µ m, blow molded film |
MPa | ||
拉伸强度 tensile strength |
|||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
2、Silica |
【新闻资讯】查看全部
两种索尔维Ryton® PPS牌号经过饮用水接触监管审批