牌号简介 About |
---|
sarlink TPV 4700系列是非常高流量的注塑工程级产品,具有优异的抗紫外线、弹性和表面美观性,适用于要求苛刻的汽车应用,包括车窗密封和外部零件。Sarlink® TPV X4765B42是一种黑色、中等硬度、低密度热塑性硫化胶,适用于需要优良流动性能的注塑应用。 The Sarlink TPV 4700 Series are very high flow injection molding engineering grades with excellent UV resistance, elasticity, and surface aesthetics designed for demanding automotive applications including window encapsulation and exterior parts. Sarlink® TPV X4765B42 is a black, medium hardness, low density thermoplastic vulcanizate suited for injection molding applications that require superior flow properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.908 | g/cm³ | ASTM D792 |
密度 Density |
0.910 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,100% 应变 TD, 100% strain |
2.30 | MPa | ASTM D412 |
TD,100% 应变 TD, 100% strain |
2.30 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
2.90 | MPa | ASTM D412 |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D412 | |
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD TD |
kN/m | ASTM D624 | |
TD TD 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ASTM D2240 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
|||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ASTM D573 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ASTM D573 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 - TD Changes in tensile stress when fractured in air - TD |
|||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ISO 188 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
体积变化 Volume change |
|||
135℃,70 hr,in IRM 903 Oil 135℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
135℃,70 hr,in IRM 903 Oil 135℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ASTM D3835 | |
200℃ 200℃ |
Pa·s | ISO 11443 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
力劲全电机助力医疗注塑新技术——第四届 CPRJ 医用橡塑技术论坛
2021-11-11 搜料网资讯: 近日,第四届CPRJ医用橡塑技术论坛暨展示会在上海举办。 包括 汉高 (中国)投资有限公司、 力劲集团 等在内的塑料产业链上下游企业代表、技术专家等与会,共 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |