牌号简介 About |
---|
AMPLIFY™ TY 1053H功能性聚合物是一种马来酸酐接枝(MAH)聚合物浓缩物,设计用于未改性聚乙烯的混合组分。在软包装的连接层中,AMPLIFY™ TY 1053H功能性聚合物促进聚乙烯与阻隔性聚合物(如聚酰胺和乙烯-乙烯醇(EVOH))的粘合。这种聚合物的功能性还促进金属、聚烯烃、纤维素、聚酯、聚碳酸酯、玻璃和箔之间的粘合。EVOH和尼龙的聚乙烯降粘树脂的典型掺合量分别为12-20%和6-12%。主要特点:顺丁烯二酸酐改性高密度聚乙烯(HDPE)胶粘剂浓缩物,用于吹塑、浇铸和涂层应用,食品包装的连接层和多层柔性薄膜应用的管道涂层粘合层聚合物相容剂符合:美国FDA 21 CFR 177.1520(c)6 EU,编号10/2011有关完整的DETA,请参考相关规定。ILS。 AMPLIFY™ TY 1053H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene. In tie layers for flexible packaging, AMPLIFY TY 1053H Functional Polymer promotes adhesion of polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Typical blending levels in polyethylene let-down resin are 12-20% for EVOH and 6-12% for nylon. Main Characteristics: Maleic anhydride modified HDPE Adhesive concentrate for use in blown, cast, and coating applications Tie layer for food packaging and pipe coating Adhesive layer in multi-layer flexible film applications Polymer compatibilizer Complies with: U.S. FDA 21 CFR 177.1520(c)6 EU, No 10/2011 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.958 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238,ISO 1133 |
MAH 接枝水平 MAH grafting level 2 |
Very High | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
129 | ℃ | ASTM D1525 , ISO 306 |
熔融温度 Melting temperature |
|||
DSC DSC |
130 | ℃ | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 , ISO 868 | ||
邵氏 A Shaw's A |
ASTM D2240 , ISO 868 | ||
邵氏 D Shaw's D |
ASTM D2240 , ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/51 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/51 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790A , ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt%, Very High >1.0 wt%. |
3 2.0 in/min |
【新闻资讯】查看全部
3D打印人造卵巢开启生殖医学新纪元
2021-04-11 搜料网资讯: 日前,美国西北大学的科学家们使用一台3D打印机制造了一个人造卵巢,并将其植入一个原有卵巢已经被切除的小鼠,该小鼠后来成功受孕。科学家们在内分泌学年会ENDO |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |