牌号简介 About |
---|
92001W是一种1-己烯-LLDPE共聚物吹塑成膜级,采用球化技术生产。此等级可用于粘合层压膜应用。92001W不含防滑和防堵塞添加剂。 92001W is a 1-Hexene LLDPE copolymer blown film grade produced by the Spherilene Technology. This grade can be used in Adhesive Lamination Film Applications. 92001W is without Slip and Antiblocking additives. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness 3 |
|||
测试 test 3 |
55 | µm | |
拉伸强度 tensile strength 4 |
ASTM D882 | ||
MD,屈服,55 µm MD, yield, 55 µ m |
10.0 | MPa | ASTM D882 |
TD,屈服,55 µm TD, yield, 55 µ m |
10.0 | MPa | ASTM D882 |
MD,断裂,55 µm MD, fracture, 55 µ m |
MPa | ASTM D882 | |
TD,断裂,55 µm TD, fracture, 55 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,55 µm MD, fracture, 55 µ m |
% | ASTM D882 | |
TD,断裂,55 µm TD, fracture, 55 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 5 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:55 µm MD:55 µm |
g | ASTM D1922 | |
TD:55 µm TD:55 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60° 60° |
ASTM D2457 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 BUR - 2.5, Die Gap - 2.5 mm |
4 20 in/min |
5 F50, 38 mm Dart, 66-cm. Height |
【新闻资讯】查看全部
德国推出新塑料打印技术工艺改良带来的惊艳效果
2017-10-10 总部位于德国的工业3D打印机制造商voxeljet宣布推出用于其VX200系统的新型塑料3D打印工艺――PolyPor C 2 (PPC2)。据悉,该技术是公司现有的PolyPor B(PPB)工艺的改进,主要用于制造金属部件的铸件。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |