牌号简介 About |
---|
20%玻璃纤维增强聚碳酸酯。一些浅色等级的影响数据可能比自然和黑色等级低。也称为:lnp*Thermocomp*化合物DF004RXP产品再订购名称:DF004RXP LNP* Thermocomp* DF004RXP is a compound based on Polycarbonate resin containing 20% Glass Fiber. Some light color grades may have lower impact data than natural and black. Added features include: Mold Release, UL |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD:24 hrs MD:24 hrs |
0.20 到 0.40 | % | |
TD:24 hrs TD:24 hrs |
0.60 到 0.80 | % | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
0.13 | % | ASTM D570 |
23℃,24hr 23℃,24hr |
0.17 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture 5 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 6 |
MPa | ASTM D790 | |
-- -- 7 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 8 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 9 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 10 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 11 |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃,Light & White Colors 23℃,Light & White Colors |
J/m | ASTM D256 | |
23℃,Natural & Black Colors 23℃,Natural & Black Colors |
J/m | ASTM D256 | |
23℃ 23℃ 12 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 13 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
-- -- |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 14 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ||
TD:-30~30℃ TD:-30~30℃ |
1/℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75-3.00 mm 0.75-3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 2 mm/min |
8 80*10*4 |
9 80*10*4 mm |
【新闻资讯】查看全部
冬季易造成安装不稳,应做好防护措施
2018-06-13 夏季高温,雷雨频发,易给装置安全稳定运行带来不利影响。扬子石化烯烃厂提前布局,早作准备,多措并举,落实好装置过夏安全稳定生产保障措施,把各种不安全、不稳定因素尽早消灭在萌芽状态,为装置过夏设置好“防护网”。 扬子石化烯烃厂提前对全厂各套装置循环水泵、凉水塔风机、水换热器、冰机等装置过夏关键设备切出清理、检修。对夏季高温天气可能会影响生产的在运和备用机泵润滑油系统、冷却水系统进行全面仔细检查,做好备用机泵定期盘车,确保机泵完好运行、完好备用。与此同时,烯烃厂做好装置中控室及生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |