牌号简介 About |
---|
SABIC PP化合物7450 SABIC® PPcompound 7450是一种矿物填充改性聚丙烯,通常用于汽车外部应用。材料性能包括良好的流动性、高冲击性、良好的刚度和低CLTE。该材料可用作化合物,但也可通过将SABICPP化合物MB7450和SABICPP 90910在成型机上按1:1比例组合而获得。SABIC® PPcompound 7450是指定的汽车级。SABIC PP化合物7450 SABIC PP化合物7450是一种矿物填充、冲击改性的聚丙烯TPO。这种材料在汽车外部应用中具有很高的抗冲击性和良好的油漆性能。IMDS是87784390。 SABIC® PPcompound 7450 is a mineral filled modified polypropylene typically used in automotive exterior applications. Material properties include good flow, high impact, good stiffness and low CLTE. This material is available as compound but can also be obtained by combining SABIC®PPcompound MB7450 and SABIC®PP 90910 on the molding machine in a 1 to 1 ration. SABIC® PPcompound 7450 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.968 | g/cm³ | ASTM D792 |
密度 Density |
0.970 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
22 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
Internal Method | ||
TD:80℃,1 hrs TD:80℃,1 hrs |
1.2 | % | 内部方法 |
TD:23℃,48 hrs TD:23℃,48 hrs |
1.0 | % | 内部方法 |
MD:80℃,1 hrs MD:80℃,1 hrs |
% | 内部方法 | |
MD:23℃,48 hrs MD:23℃,48 hrs |
% | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 3 |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
50 mm跨距 50 mm span 5 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 7 |
ISO 179/1eA | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ISO 180/1A | ||
23℃,3.2mm 23℃,3.2mm 8 |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
ISO 180/1A | ||
23℃ 23℃ |
ISO 180/1A | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
|||
23℃,3.2 mm 23℃,3.2 mm 8 |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 6 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 6 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 6 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 方法 I (三点负荷) |
7 80*10*4mm, Cut |
8 80*10*4 mm, Cut |
9 63.5*12.7*3.2mm, Cut |
10 7.22 ft/sec |
【新闻资讯】查看全部
扬州晨化2020年净利1.37亿元 5000吨聚醚胺项目6月底投入使用
2021-05-03 搜料网资讯: 4月24日,扬州 晨化 发布2020年及2021年一季度业绩公告:2020年实现营业收入9亿元,同比增长11.85%;净利润1.37亿元,同比增长44%。业绩增加主要原因是子公司淮安晨化产能逐 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |