BC 7020是一种轻质双组分环氧回填系统。与BC 7010不同,填料部分预先混合到树脂和硬化剂成分中,以便于搬运,从而简化混合过程。BC 7020非常适用于涉及模具和型芯结构的铸造应用。BC 7020具有以下优点:低成本简单配合比(1:1重量比),使用寿命长,可机械加工,收缩率低,变色,确保完全混合 BC 7020 is a lightweight two component epoxy backfill system. Unlike BC 7010, the filler portion is pre-blended into the resin and hardener components for easier handling, thus simplifying the mixing process. BC 7020 is ideally suited for foundry applications involving mold and core construction. BC 7020 features the following advantages: Low cost Simple mix ratio (1 to 1 by wt.) Long pot life Machineable Low shrinkage Color change to insure complete mix |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.780 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD MD |
0.020 | % | ASTM D2566 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
53.3 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
Blue | ||
-- -- 3 |
Green | ||
-- -- 4 |
|||
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Resin Resin |
|||
Hardener Hardener |
|||
固化时间 Curing time |
|||
24℃ 24℃ |
hr | ||
储存稳定性 storage stability |
|||
24 ℃ 24 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,24℃ Shaw's D, 24 ℃ |
|||
压缩强度 compressive strength |
MPa |
备注 |
---|
2、Resin |
3、Mixed |
4、Hardener |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |