牌号简介 About |
---|
聚甲醛(POM)共聚物,强流动型,用于注塑和挤出成型,具有较高的冲击韧性和耐高温跟踪性;对溶剂、燃料和强碱具有良好的耐化学性,以及良好的水解性;具有较高的耐热性和氧化降解性。该等级经过特殊稳定处理,以防止因紫外线照射而引起的变色和机械性能恶化。这种材料有天然的、黑色的和彩色的。厚度大于1 mm时,燃烧速率为ISO 3795和FMVSS 302<75 mm/min。应用范围:注射成型厚壁、无空隙的成型零件;挤出,例如用于板材和管道。联邦机动车辆安全标准(美国) POM copolymer Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. This grade has been specially stabilized to prevent discoloration and deterioration of mechanical properties from ultraviolet light exposure. The material is available in natural, black and colored. Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes. FMVSS = Federal Motor Vehicle Safety Standard (USA) |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2600 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服 yield |
62.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
9.0 | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 Nominal tensile fracture strain |
32 | % | ISO 527-2/1A/50 |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
2300 | MPa | ISO 899-1 |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
Density of Melt Density of Melt |
g/cm³ | Internal Method | |
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | Internal Method | |
Thermal Conductivity of Melt Thermal Conductivity of Melt |
W/m/K | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
【干货】PVC材料常见改性方法及应用
2021-03-11 搜料网资讯: PVC改性介绍 聚氯乙烯(PVC或乙烯基)是一种经济和通用的热塑性聚合物,广泛用于建筑和建筑行业、生产门窗型材、管道(饮用水和废水)、电线电缆绝缘、医疗设备等。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |