牌号简介 About |
---|
3M Dyneon聚四氟乙烯细粉TF 2072Z推荐用于制造小型管道、电线和电缆绝缘。特殊特性符合ASTM D 4895 I型1级C类高分子量聚四氟乙烯粉末,由乳液聚合生产,由于还原率(RR)范围大,加工窗口宽,降低了润滑油消耗(与TF 2071Z相比,每100重量份聚四氟乙烯减少1重量份),更经济的膏体挤出工艺。由于更大的可用预成型,具有优异的化学惰性、低摩擦性能、高阻燃性、优异的耐温性、很好的电气性能,由于较低的压力水平,减少了挤出机的负荷。 Dyneon™ TF 2072 Z PTFE is an ideal grade for thin-wall, small diameter tubing and wire and cable insulations, processed by paste extrusion method at reduction ratio up to 3000:1. This product offers more economic processing because of larger usable preforms. Product Features: High molecular weight Needs less lubricant than TF 2071 Z (1-2 parts by weight) Emulsion polymerization PTFE Product grade with lower extrusion pressure than TF 2071 Z Meets ASTM D4895-04 Type 1, Grade 1, Class C classification Processing by standard paste extrusion methods |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 1 |
2.17 | g/cm³ | ISO 12086 |
表观密度 Apparent density |
0.47 | g/cm³ | ISO 60 |
平均颗粒尺寸 Average particle size |
440 | µm | ISO 13320 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
35.0 | MPa | ISO 527-3 |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
470 | % | ISO 527-3 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
挤出压力 Extrusion pressure |
|||
Reduction Ratio 1600 Reduction Ratio 1600 |
MPa | ASTM D4895 | |
Reduction Ratio Reduction Ratio |
内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
OPEC会议前瞻:俄罗斯沙特提前达成一致?两大痛点困扰油价
2021-03-30 搜料网资讯: 周一国际油价探底回升,石油输出国组织(OPEC)可能继续延长现有减产协议的消息抵消了苏伊士运河恢复通行及欧洲地区疫情反复的利空影响。OPEC+即将举行部长级会议, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |