牌号简介 About |
---|
CALIBRE™ 603-6 聚碳酸酯树脂是一种接枝的聚碳酸酯,是专为多壁层结构的片材挤出加工而研制的。CALIBRE 603-6 具有较高的熔体强度,可以对很多种类的多壁层片材结构进行有效地定型,这些结构的复杂程度从低至高,复杂程度高的比如7层结构的片材。与CALIBRE 503-5相比,CALIBRE 603-6的加工窗口更宽,因此在高速生产线上它可以赋予片材以优异的表面质量,减少出现震痕的倾向。CALIBRE 603-6含有紫外线吸收剂,但是请注意室外用板材还需要一层吸收紫外线的保护层。推荐使用CALIBRE™ 320UV 与其共挤出,制造出一个厚度为50 µm的保护层。 主要特性: 加工窗口宽 表面质量高 可将震痕减低至最低水平 应用领域: 低复杂度和高度复杂的多壁层结构的片材。 CALIBRE™ 603-6 Polycarbonate Resin is a branched polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 603-6 offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to high complexity, such as seven wall sheet. CALIBRE 603-6 offers a wider processing window than CALIBRE 503-5 and is likewise specially designed to give excellent sheet surface quality at high line speeds with a reduced tendency to display chatter marks. CALIBRE 603-6 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV. Main Characteristics: Wide processing window High surface quality Minimizes chatter marks Applications: Low to high complexity multi-wall sheets |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
6.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.15 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm,解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 3 |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 3 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
茂名石化聚丙烯高端产品成功开拓欧美市场
2021-12-23 搜料网资讯: 12月7日,茂名石化透明聚丙烯系列高端产品通过美国安全检测实验室公司(UL)认证,符合国际绿色环保可持续要求,成功开拓透明聚丙烯系列高端产品欧美市场。 UL绿色 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |