牌号简介 About |
---|
Bi300是一种结晶度较高的高等规嵌段共聚物,与普通聚丙烯相比,由于其结晶性好,橡胶设计最佳,因此在高硬度和冲击强度之间具有良好的性能平衡。由该等级制成的薄膜具有很高的耐热性和优越的机械强度,因此该等级非常适合于干馏袋薄膜的应用。 Description BI300 is a high isotactic Block Copolymer which has higher crystallinity, compared to general PP. Due to high crystalline nature & optimum rubber design, BI300 has an excellent property balance between high stiffness and impact strength. Films made from this grade provide high heat resistance and superior mechanical strength, thus this grade is highly suited to retort pouch film application. Characteristics Good balance physical property between stiffness & impact strength Punch resistance Heat resistance High transparency Applications Retort pouch, Cast film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
3.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
60 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture 2 |
23.5 | MPa | ASTM D638 |
MD,屈服,60 µm MD, yield, 60 µ m |
22.6 | MPa | ASTM D882 |
TD,屈服,60 µm TD, yield, 60 µ m |
20.6 | MPa | ASTM D882 |
MD,断裂,60 µm MD, fracture, 60 µ m |
MPa | ASTM D882 | |
TD,断裂,60 µm TD, fracture, 60 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture 2 |
% | ASTM D638 | |
MD,断裂,60 µm MD, fracture, 60 µ m |
% | ASTM D882 | |
TD,断裂,60 µm TD, fracture, 60 µ m |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
0℃ 0℃ |
J/m | ASTM D256 | |
5℃ 5℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
熔融温度 Melting temperature |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
60 µm 60 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 压 力1 (10N) |
【新闻资讯】查看全部
白宫宣布美国史上最大战略油储释放计划:半年里每天释放100万桶石油
2022-04-01 3月31日周四,美国白宫发布能源相关措施的情况说明书,称总统拜登将宣布美国历史上最大规模的战略石油储备(SPR)释放计划。 计划显示,美国将每天释放100万桶石油,持续六个月时 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |