牌号简介 About |
---|
LTP CE-2200系列树脂是一种基于聚苯硫醚(PPS)的高性能工程塑料。由于其优良的导电性能,主要应用于电热仪表恒温件或外壳。LTP CE-2200系列树脂制导热保温材料具有控温精度高、耐水、耐油、安全性好、重量轻、耐磨性好等特点。 Resin of LTP CE-2200 serials is a kind of engineering plastic with high performance based on PPS. For its excellent electric conduction property, it is mainly applied in thermostatic parts or shell for electric heating instrument. Thermal conduction and insulation materials made by Resin of LTP CE-2200 serials have these characteristic: high temperature control precise, resistance to water, oil-proof, good safety, light weight and wear well. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 到 1.90 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate 2 |
|||
3.0 mm 3.0 mm 2 |
0.50 到 0.80 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
100 到 125 | MPa | GB/T 1040 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
1.2 | % | GB/T 1040 |
弯曲模量 Bending modulus |
80000 | MPa | GB/T 1042 |
弯曲强度 bending strength |
MPa | GB/T 1042 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | GB/T 1043 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
℃ | GB/T 1634 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | GB/T 1410 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 80x80x3 mm |
【新闻资讯】查看全部
注射成型时气泡发生缘由及措施
2016-07-20 模具主要是对工件进行研制的工具,其在工件注射成型过程中,我们会发现一些气泡的形成,注塑成型中出现气泡容易导致工件熔炼痕,而导致这种现象产生的原因以及解决措施,中华标准件网进行详细介绍。 原因一:在制品壁厚较大时,其外表面冷却速度比中心部的快,因此,随着冷却的进行,中心部的树脂边收缩边向表面扩张,使中心部产生充填不足。这种情况被称为真空气泡。 解决措施主要有: 1、根据壁厚,确定合理的浇口,浇道尺寸。一般浇口高度应为制品壁厚的50%~60%。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |