牌号简介 About |
---|
Tecapetpet是一种从聚对苯二甲酸乙二醇酯衍生而来的无增强半结晶热塑性聚酯。其优异的耐磨性、低摩擦系数、高弯曲模量和优越的尺寸稳定性使其成为设计机械和机电零件的通用材料。由于Tecapetpet没有中心孔,因此几乎消除了流体吸收和泄漏的可能性。Tecapetpet优越的耐磨性和中心线孔的缺乏使其在涉及溶剂、化学品和食品的应用方面优于其他材料。Tecapetpet还用于水净化系统、印刷设备、纺织部件、食品处理设备和阀门。 TECAPET®PET is an unreinforced, semicrystalline thermoplastic polyester derived from polyethylene terephthalate. Its excellent wear resistance, low coefficient of friction, high flexural modulus, and superior dimensional stability make it a versatile material for designing mechanical and electro-mechanical parts. Because TECAPET®PET has no centerline porosity, the possibility of fluid absorption and leakage is virtually eliminated. TECAPET™PET superior wear resistance and lack of centerline porosity give it an advantage over other materials for applications involving solvents, chemicals, and food products. TECAPET™PET is also used in water purification systems, printing equipment, textile components, food-handling equipment, and valves. Excellent wear resistance Low coefficient of friction Very good chemical resistance No centerline porosity eliminates the possibility of fluid absorption and leakage Good electrical insulator High mechanical strength Excellent hardness and stiffness Good weather resistance Low water absorption Good resistance to high-energy radiation |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.38 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
ASTM D570 | ||
23℃,24hr 23℃,24hr |
0.10 | % | ASTM D570 |
饱和,23℃ Saturation, 23 ℃ |
0.50 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
37 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
116 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
比热 specific heat |
J/kg/℃ | ||
最高使用温度 Maximum operating temperature |
|||
Intermittent Intermittent |
℃ | ||
长期 long-term |
℃ | UL 746B | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 4 |
|||
23 ℃,60 Hz 23 ℃,60 Hz 4 |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
23℃,60 Hz 23℃,60 Hz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic 2 |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
磨损因数 Wear factor 3 |
|||
0.28 MPa,0.25 m/sec 0.28 MPa,0.25 m/sec 3 |
10^-8 mm³/N·m | ASTM D3702 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 40 psi, 50 fpm |
3 Against Steel |
4 50% RH |
【新闻资讯】查看全部
三井化学韩国子公司开端运转
2016-04-06 三井化学宣布旗下新建子公司,三井化学(韩国)公司将于2016年4月1日正式运行。 新公司由三井化学韩国子公司重建而成,最初于2014年10月1日建成。 新公司将组建一个优化型销售网络,进一步扩大三井化学在韩国的业务范围,主要服务于汽车以及电子电气行业。 三井化学公司,是根据1996年达成的协议,于1997年10月1日由日本三井石油化学工业公司和三井东压化学公司合并成立的。三井化学公司按其合并的销售额计算,是日本第二大综合性化工公司,在世界大石 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |