牌号简介 About |
---|
新Plasti-Paste® II是一种双组分纤维填充树脂,设计用于垂直表面应用。这种无气味配方是我们原来的塑料糊配方的改进版本,固化产品在以下方面有所不同:1。Plasti-Paste® II现在不含邻苯二甲酸盐。2.第2条。固化后的塑料可涂(原塑料糊不能涂)和3。它更硬,更硬,耐热性更好。A部分是液体,B部分是糊状物。新的配合比为体积比1a:2b(重量比62a:100b)。室温下的适用期为10分钟,取决于质量。在室温下(取决于质量),拆卸时间(可处理)约为90分钟。完全固化;室温下24小时。加热可以加速固化时间。混合材料保持一个垂直的表面没有下垂和固化成一个强大,耐用和轻塑料。液体材料可以从光滑的表面涂上如此强烈的色彩。这种塑料可用于创建主题环境或特殊效果,用作“母模”材料,以加强橡胶模具和各种其他应用。这种塑料也是一种强大的粘合剂,可作为各种工业应用的修补材料。固化后的塑料可以用砂纸打磨、机加工,然后用丙烯酸瓷漆上漆。 New Plasti-Paste® II is a two component fiber-filled resin that is designed for vertical surface application. This no-odor formulation is an improved version of our original Plasti-Paste® formula, and the cured product is different in the following ways: 1. Plasti-Paste II is now phthalate free. 2. Cured plastic can be painted (original Plasti Paste® can not) and 3. It is harder, more rigid with better heat resistance. Part A is a liquid and Part B is a paste. New Mix Ratio is 1A: 2B by volume (62A:100B by weight). Pot life is 10 minutes at room temperature depending on mass. Demold time (can be handled) is about 90 minutes at room temperature depending on mass. Full cure; 24 hours at room temperature. Cure time can be accelerated by applying heat. Mixed material holds a vertical surface without sagging and cures to a strong, durable and lightweight plastic. Liquid material can be pigmented with So-Strong® color tints from Smooth-On. This plastic can be used for creating themed environments or special effects, used as a "mother mold" material to reinforce rubber molds and a variety of other applications. This plastic is also a powerful adhesive and can be used as a repair material for a variety of industrial applications. Cured plastic can be sanded, machined and painted with acrylic enamel paints. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.998 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
1.00 | cm³/g | ASTM D1475 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 | % | ASTM D2566 |
粘度 viscosity |
Paste | ASTM D2393 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
1A:2B by volume 62A:100B by weight | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 | |
脱模时间 stripping time |
|||
23℃ 23℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
安徽省质监局通报塑料管材省级监督抽查结果
2016-11-25 近日,安徽省质监局通报了2016年塑料管材省级监督抽查结果,共抽取了40组样品,2组样品不合格,抽样合格率为95.0%。 安徽省质监局通报塑料管材省级监督抽查结果 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |