牌号简介 About |
---|
优异的环境应力抗裂性、优异的型坯熔融强度/低凹陷性、良好的挤出性/加工性、良好的刚性符合美国FDA 21 CFR 177.1520(c)3.2A符合加拿大HPFB。无异议(有限制)符合欧盟10/2011号条例。有关完整的详细信息,请参阅条例。UNIVAL™ DMDC-6143 NT 7高密度聚乙烯(HDPE)树脂是一种具有广泛分子量分布和高分子量聚合物的聚合物。该产品具有良好的稳定性,有助于大部件壁厚均匀,非常适合于容器的吹塑成型,如5-30加仑(19-114升)的密封头桶和其他大部件。该树脂分子量分布广,具有优异的抗环境应力开裂性能、良好的刚性和挤出性。 Outstanding environmental stress crack resistance Excellent parison melt strength / low sag Good extrudability / processability Good rigidity Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Complies with Canadian HPFB No Objection (With Limitations) Complies with EU, No 10/2011 Consult the regulations for complete details. UNIVAL™ DMDC-6143 NT 7 High Density Polyethylene (HDPE) Resin is a polymer with broad molecular weight distribution and high molecular weight polymer. This product provides good stability, which contributes to uniform wall thickness in large parts, making it ideal for blow molding of containers, such as the 5-30 gallon (19-114 liter) tight-head pails, and other large parts. The broad molecular weight distribution of this resin contributes to the outstanding environmental stress crack resistance (ESCR), good rigidity level and extrudability it offers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
14 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
1100 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 3 |
357 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
67.0 | ℃ | ASTM D648 |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-B |
备注 |
---|
1 With limitations |
2 一般属性:这些不能被视为规格。 |
3 类型 S |
【新闻资讯】查看全部
塑料制品的实践使用技巧
2017-10-20 一、定方案 根据塑料不同的性能、工艺、特性、原则、产品要求等,我们在制作塑料制品的时候,要进行综合的考虑,并且对各种的色粉进行拼色处理,然后达到所需要的颜色的要求。任何颜色,它都具有一定的色相,一定的明亮度,以及一定的饱和度,通过改变这三个因素我们就可以调配出数以万计的颜色。所以,在调色中,如何掌握色调的深浅、色相、色差这三个技巧是我们需要掌握的基本技术。调色的原则是先调深浅再调色相,因为深浅颜色一变,色相就肯定变了。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |