牌号简介 About |
---|
玻璃纤维增强硅酮化合物具有优异的热稳定性-连续使用温度高达300°C,特殊的电气性能,良好的机械强度,非常好的尺寸稳定性-主要应用:非常高的耐热连接器-本产品满足重金属和PCA以及C的允许上限。符合欧盟指令2002/95(RoHS)、2002/96(WEEE)和2006/122(PFOS)的要求 Glass-fibre reinforced silicone compound Excellent thermal stability - continual use temperatures of up to 300 °C, exceptional electrical properties, good mechanical strength, very good dimensional stability Primary application(s): Very high heat resistant connectors This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
2.10 到 2.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density Apparent density |
0.95 到 1.05 | g/cm³ | ISO 60 |
成型收缩率 Molding Shrinkage Molding shrinkage |
ISO 2577 | ||
MD MD |
0.20 到 0.60 | % | ISO 2577 |
MD MD |
0.40 到 0.80 | % | ISO 2577 |
吸水率 Water Absorption Water Absorption |
|||
23℃,24hr 23℃,24hr |
< 0.10 | % | ISO 62 |
后收缩 after shrinkage After shrinkage |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
|
MPa | ISO 527-2 | |
拉伸强度 Tensile Strength Tensile Strength |
|||
|
MPa | ISO 527-2 | |
弯曲模量 Flexural Modulus Flexural Modulus |
|||
|
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
|||
|
MPa | ISO 178 | |
压缩强度 Compressive Strength Compressive Strength |
MPa | ISO 604 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
|
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
|
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:50~150℃ MD:50~150℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal Conductivity Thermal conductivity |
W/m/K | ASTM E1461 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface Resistivity Surface Resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume Resistivity Volume Resistance |
ohms·cm | IEC 60093 | |
介电强度 Dielectric Strength Dielectric Strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative Permittivity Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation Factor Dissipation Factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc Resistance Arc Resistance |
ASTM D495 | ||
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.60 mm,Tested by RASCHIG 0.60 mm,Tested by RASCHIG |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Compression Molded |
3 Injection Molded |
4 168 h / 110°C |
【新闻资讯】查看全部
Teknor Apex 与安踏联手开发出高回弹性中底
2020-10-28 搜料网资讯: Teknor Apex Company采用定制的配方所生产的热塑性弹性体(TPE)帮助中国安踏体育用品有限公司开发出一款表现卓越的高回弹性能的跑鞋,用户穿着这款跑鞋能够更轻松地跑出更 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |