牌号简介 About |
---|
聚丙烯自熄化合物,均聚物20%滑石填充,按UL-94、V-2标准分类,低卤素含量。不含PBDE。不含锑和重金属。高温下使用的热稳定性。高流动性和刚度,特别适用于需要良好的平面性和尺寸稳定性和含收缩的应用。可根据样品选择自然色和彩色。 Polypropylene self-extingusihing compound, homopolymer 20% talc filled; classifiable according to the norms of UL-94, V-2; low halogen content. Free from PBDE. Free from antimony and heavy metals. Thermal stabilization for use at high process temperatures. High flowability and stiffness, specific for applications where good planarity and dimensional stability with contained shrinkage are required. Available in the versions natural and colored as per sample. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
13 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.2 | % | ISO 294-4 |
MD MD |
1.2 | % | ISO 294-4 |
灰份含量 Ash Content |
20 | % | ISO 3451 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速烘箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
day | ISO 4577 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 335 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 3 |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
4.0 mm 4.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
4 mm 4 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/20 | |
拉伸应变 Tensile strain |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/20 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 IDONEO |
【新闻资讯】查看全部
调整“限塑令”并非复杂地扩展限塑范围
2018-01-16 2007年发布的“限塑令”执行已有10年,虽然相关方面给出的数据显示,过去10年间,超市、商场的塑料袋使用量普遍减少2/3以上,累计减少塑料袋140万吨左右,相当于节约了840万吨石油,但是,这些来之不易的成绩还是掩盖不了“限塑令”所面临的自身难以克服的尴尬与窘境。 “限塑令”主要针对商品零售场所的塑料购物袋,限制使用范围明显有限不说,加上有法不依、执法不严现象普遍存在,“限塑令”在一些地方可以说是名存实亡,“限白”几乎成了“白限”。尤其是自购物塑料袋有偿使用以来,两三毛钱 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |