牌号简介 About |
---|
低模量薄膜与聚丙烯和聚乙烯具有良好的相容性,符合美国FDA 21 CFR 177.1520(c)3.1a,符合欧盟第10/2011号法规,详情请参考相关法规。采用道氏气相聚合法制备了DFDA-1010NT7超低密度聚乙烯(VLDPE)树脂。这是一种乙烯-丁烯共聚物,具有很高的柔韧性和弹性。它可用于单层和共挤薄膜以及与其他聚烯烃的混合物中,以增强结构的韧性。 Low modulus film Excellent compatibility with polypropylene and polyethylene Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Complies with EU, No 10/2011 Consult the regulations for complete details. DFDA-1010 NT 7 Very Low Density Polyethylene (VLDPE) Resin is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance toughness of the structure. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.906 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.85 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
20 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
-38.9 | ℃ | 内部方法 |
熔融温度 Melting temperature |
|||
DSC DSC |
119 | ℃ | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,1 秒 Shore A, 1 second |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
全国首个化学中毒救治远程平台启建
2021-07-20 搜料网资讯: 7月16日,长三角区域职业健康合作协议签约仪式暨长三角化学中毒远程协作中心建设启动会在合肥召开。根据协议,沪苏浙皖三省一市卫生健康行政部门将积极推动职业健 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |