牌号简介 About |
---|
PULSE™ 2100LG 工程树脂在需要高韧性的应用领域具有最好的性能表现,这些应用从单件物品到复杂零部件均有涉及。PULSE 2100LG 可以承受极高和极低的温度,在快速的、重复性的温度波动下,也有良好的性能表现。 特点: 低光泽 -20°F 延展性 性能范围宽 优异可加工性 批次稳定性 耐化学性 PULSE™ 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations. Benefits: Low gloss appearance Low temperature ductility Wide range of performance Superior processability Lot to lot consistency Good chemical resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
密度 Density |
1.13 | g/cm³ | ISO 1183/B |
密度 Density |
1.13 | g/cm³ | ISO 1183-2 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,3.80kg 260℃,3.80kg |
4.5 | g/10min | ISO 1133 |
230℃,3.80kg 230℃,3.80kg |
4.5 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,3.8 kg 230℃,3.8 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
% | ISO 294-4 | |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ASTM D638 | |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2 2 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 2 | |
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA 2 | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 2 | |
简支梁冲击强度 Charpy impact strength |
|||
23℃ 23℃ |
ISO 179/1eU 2 | ||
-30℃ -30℃ |
ISO 179/1eU 2 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃,3.2mm,注塑成型 -30 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃ -40℃ |
kJ/m² | ISO 180 | |
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-29℃,3.20 mm,Peak Energy -29℃,3.20 mm,Peak Energy |
J | ASTM D3763 | |
23℃,3.20 mm,Peak Energy 23℃,3.20 mm,Peak Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 2 | |
-- -- |
℃ | ISO 306/A120 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
MD MD |
1/℃ | ISO 11359-2 2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,Smooth 60°,Smooth |
ASTM D542 | ||
GMCP88(Light Stipple) GMCP88(Light Stipple) |
% | ASTM D542 | |
Monticello Monticello |
% | ASTM D542 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
3 21,7 ft/sec |
4 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
石大胜华牵手中化泉州投建新能源材料项目
2022-04-10 石大胜华10月13日晚间公告,公司拟与中化泉州石化有限公司合作在福建泉州投资建设年产44万吨的新能源材料项目,该项目总投资13亿元,其中一期投资7.94亿元。 据公告,项目将分两期进行 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |