牌号简介 About |
---|
丙烯在复杂的有机金属催化剂作用下聚合得到的产物。它包括长期热稳定性的提高,生产、加工和开发聚丙烯制品时的热氧化降解抗性,制品对环境变色的抗性更高。用途:平槽挤出膜,管状膜,膨体连续长丝及螺纹。技术要求:TU 2211-136-05766801-2006 Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates enhanced long-term thermal stability, thermal-oxidative degradation resistance at PP production, processing and use of PP-made articles, improved resistance to fading from environmental exposure. Application: flat-slot extrusion film, tubular film, bulk continuous filament and filament yarn. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | |
表观密度 Apparent density |
0.48 到 0.52 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
30 到 40 | g/10min | ASTM D1238 |
灰份含量 Ash Content |
0.025 到 0.050 | % | |
凝胶含量 Gel content 2 |
|||
> 200.0 µm > 200.0 µm |
250 | pcs/m² | |
0.700 到 1.50 mm 0.700 to 1.50 mm |
pcs/m² | ||
1.50 到 2.50 mm 1.50 to 2.50 mm |
pcs/m² | ||
> 2.50 mm > 2.50 mm |
pcs/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp 3 |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Thermal Creep Temperature Thermal Creep Temperature 4 |
℃ | ||
热氧化恶化 Thermal oxidation deterioration |
|||
150℃ 150℃ |
day | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
|||
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 p.4.8 TU 2211-136-05766801-2006 |
3 in liquid medium under force 10 H |
4 at load 0.46 H/mm² |
【新闻资讯】查看全部
提高涂料和粘合剂的性能,索尔维推出新型乳化剂
2022-11-29 扫描上图二维码,可以免费下载 搜料 APP 近日,索尔维推出Reactsurf2490,是一种新型无APE可聚合表面活性剂,被设计为丙烯酸,乙烯-丙烯酸和苯乙烯-丙烯酸乳液体系的主要乳化剂。与传 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |