牌号简介 About |
---|
Lofex A31ll是一种光学透明的聚酯薄膜,两面经过聚氨酯处理,增强了对紫外线油墨和涂层的粘附力。该产品具有优异的运行性能,易于用合适的产品进行处理,可用于硅片、保护膜、窗膜等。通过拉伸强度、适当的延伸率和热收缩率,该材料具有优良的性能。 LOFEX ® A31LL is Polyester film is optically clear and both sides urethane treated with enhances adhesion to UV ink and coatings. It can use by silicon release film, protection film, window film because it has excellent run, easy treatment by suitable product. It has excellent properties by tensile strength, proper elongation and the thermal contraction rate. |
技术参数 Technical Data | |||
---|---|---|---|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,50 µm MD, yield, 50 µ m |
196 | MPa | ASTM D882 |
MD,屈服,75 µm MD, yield, 75 µ m |
196 | MPa | ASTM D882 |
MD,屈服,100 µm MD, yield, 100 µ m |
196 | MPa | ASTM D882 |
TD,屈服,50 µm TD, yield, 50 µ m |
235 | MPa | ASTM D882 |
TD,屈服,75 µm TD, yield, 75 µ m |
216 | MPa | ASTM D882 |
TD,屈服,100 µm TD, yield, 100 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
MD,断裂,75 µm MD, fracture, 75 µ m |
% | ASTM D882 | |
MD,断裂,100 µm MD, fracture, 100 µ m |
% | ASTM D882 | |
TD,断裂,50 µm TD, fracture, 50 µ m |
% | ASTM D882 | |
TD,断裂,75 µm TD, fracture, 75 µ m |
% | ASTM D882 | |
TD,断裂,100 µm TD, fracture, 100 µ m |
% | ASTM D882 | |
F5 F5 |
ASTM D882 | ||
MD:50.0 µm MD:50.0 µm |
MPa | ASTM D882 | |
MD:75.0 µm MD:75.0 µm |
MPa | ASTM D882 | |
MD:100.0 µm MD:100.0 µm |
MPa | ASTM D882 | |
TD:50.0 µm TD:50.0 µm |
MPa | ASTM D882 | |
TD:75.0 µm TD:75.0 µm |
MPa | ASTM D882 | |
TD:100.0 µm TD:100.0 µm |
MPa | ASTM D882 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D523 | ||
60°,50.0 µm 60°,50.0 µm |
ASTM D523 | ||
60°,75.0 µm 60°,75.0 µm |
ASTM D523 | ||
60°,100 µm 60°,100 µm |
ASTM D523 | ||
透光率 Transmittance |
ASTM D1003 | ||
50.0 µm 50.0 µm |
% | ASTM D1003 | |
75.0 µm 75.0 µm |
% | ASTM D1003 | |
100 µm 100 µm |
% | ASTM D1003 | |
雾度 Haze |
ASTM D1003 | ||
50 µm 50 µm |
% | ASTM D1003 | |
75.0 µm 75.0 µm |
% | ASTM D1003 | |
100 µm 100 µm |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热收缩 Thermal shrinkage |
内部方法 | ||
MD,30 min:150℃,50.0 µm MD,30 min:150℃,50.0 µm |
% | 内部方法 | |
MD,30 min:150℃,75.0 µm MD,30 min:150℃,75.0 µm |
% | 内部方法 | |
MD,30 min:150℃,100.0 µm MD,30 min:150℃,100.0 µm |
% | 内部方法 | |
TD,30 min:150℃,50.0 µm TD,30 min:150℃,50.0 µm |
% | 内部方法 | |
TD,30 min:150℃,75.0 µm TD,30 min:150℃,75.0 µm |
% | 内部方法 | |
TD,30 min:150℃,100.0 µm TD,30 min:150℃,100.0 µm |
% | 内部方法 | |
Surface Treatment Surface Treatment |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中科院大连化物所发展出生物质合成共聚酯单体新方法
2021-12-16 搜料网资讯: 中国科学院大连化学物理研究所12月14日发布消息,近日,中国科学院院士、中科院大连化学物理研究所研究团队,发展出一种利用乙醛和丙烯酸酯的生物质合成共聚酯单体 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |