牌号简介 About |
---|
Versaflex™ HC MT222一种透明的高性能TPE材料,转为医疗导管研发。VersaflexTM HC MT222采用特制配方,不使用任何增塑剂。 新产品。还未建立商业规范。 • 柔韧 • 采用不使用增塑剂的特制配方 • 透明度高 Versaflex™ HC MT222 is an exceptionally clear, high performance TPE developed for medical tubing for healthcare. Versaflex™ HC MT222 has been specially formulated without the use of any plasticizers. Flexible Formulated without plasticizers High Clarity |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,10 秒 Shore A, 10 seconds |
66 | ASTM D2240 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透氧率 Oxygen permeability |
|||
21℃,1900 µm 21℃,1900 µm |
590 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 , 4 |
ASTM D412 | ||
断裂,23℃ Fracture, 23 ℃ 3 , 4 |
6.19 | MPa | ASTM D412 |
100% 应变,23℃ 100% strain, 23 ℃ |
2.30 | MPa | ASTM D412 |
300% 应变,23℃ 300% Strain, 73°F |
4.34 | MPa | ASTM D412 |
拉伸应变 Tensile strain 3 , 4 |
|||
断裂,23℃ Fracture, 23 ℃ 3 , 4 |
% | ASTM D412 | |
压缩形变 Compression deformation |
ASTM D395B | ||
22℃,22 hr 22℃,22 hr |
% | ASTM D395B | |
45℃,22 hr 45℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
收缩率 Shrinkage rate |
|||
MD MD |
% | ASTM D955 | |
熔体表观粘度 Apparent viscosity of melt |
ASTM D3835 | ||
200℃,1340 sec^-1 200℃,1340 sec^-1 |
Pa·s | ASTM D3835 | |
200℃,11200 sec^-1 200℃,11200 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 Please contact PolyOne GLS Thermoplastic Elastomers for a complete copy of the GLS Healthcare Policy. 1. The Customer must notify GLS of any FDA Class I and/or European Union Class I medical devices for each specific product and application. 2. The Customer shall not knowingly manufacture, use, sell or otherwise supply, directly or indirectly products or compounds made from GLS products in any of the following without prior written approval by GLS for each specific product or application: a. Cosmetics b. Drugs and other Pharmaceuticals c. Temporary or permanent implantation in the human body, regardless of the intended duration of implantation d. Class II and Class III Medical Devices as defined in 21 CFR 860.3 ("Medical Devices") e. Class IIa, IIb and III as defined in Directive 93/42/EEC |
2 一般属性:这些不能被视为规格。 |
3 C 模具 |
4 2 小时 |
【新闻资讯】查看全部
CHINAPLAS三天累计133,844人入场
2016-04-29 今届CHINAPLAS场面更加火热,三天累计人数已超2014年上海展会。 CHINAPLAS 2016今天是展会最后一天,今天是免费入场,行业人士请把握机会,快快入场。 27日是第三天展会,入场人数为38,757人,海外观众占比27.44%,累计三天人数为133,844。 2014年的上海展会,累计录得入场人数130,370。今届展会三天的入场人数,已超过去年的总人数,真正更上层楼。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |