牌号简介 About |
---|
Nusil技术的限制性材料可考虑用于短期植入应用,29天或更短时间,或用于外部应用。高稠度橡胶(HCR)是由高分子量聚合物与二氧化硅结合而成,它可以被成型、挤压或压延成有用的最终产品。HCR具有粘土的稠度,主要在一个或两个部分的系统(分别是过氧化物和铂催化剂)中配制。大多数铂固化高稠度橡胶是双组分系统,易于使用,配合比为1:1。评论:高撕裂 NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. High consistency rubber, or HCR, consists of high molecular weight polymer combined with silica to produce a material that can be molded, extruded, or calendared into a useful end product. An HCR has the consistency of clay and is primarily formulated in a one or two part system (peroxide and platinum catalysts respectively). Most platinum cure high consistency rubbers are two component systems with an easy-to-work-with 1:1 mix ratio. Comments: HIGH TEAR |
技术参数 Technical Data | |||
---|---|---|---|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
部件 A Component A |
按重量计算的混合比: 1.0 | ||
部件 B Component B |
按重量计算的混合比: 1.0 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Cure System Cure System |
Platinum | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | |
固化时间 Curing time |
|||
116℃ 116℃ |
0.17 | hr | |
储存稳定性 storage stability |
|||
25 ℃ 25 ℃ |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
拉伸强度 tensile strength |
MPa | ||
200% 应变 200% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
撕裂强度 tear strength |
kN/m |
备注 |
---|
1 一般属性:这些不能被视为规格。 |