牌号简介 About |
---|
生物复合材料是由生物塑料树脂(生物基和/或可生物降解)与天然纤维(如木材、大麻、竹子或纤维素)混合而成的一组材料。生物复合材料主要用于注塑成型,也可用于挤出成型或热成型。市场:化妆品,园艺,技术零件,运动休闲,美学零件…性能刚性好,热机械性能好。可见纤维。 Biocomposites are a set of materials consisting in a blend of a bioplastic resin (biobased and/or biodegradable) with natural fibres such as wood, hemp, bamboo or cellulose. Biocomposites are mainly designed for injection molding applications but can also be used in extrusion molding or thermoforming. Markets: cosmetics, horticulture, technical parts, sport and leisure, aesthetic parts... Properties Stiffness, good thermal and mechanical properties. Visible fibres. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
20 到 25 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1170 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
23 | % | ISO 527-2 |
弯曲模量 Bending modulus |
940 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
独石化“聚乙烯”剑指高端包装范围
2017-08-30 8月9日,独山子石化公司茂金属聚乙烯产品HPR1018HA的重包装膜加工试验在下游某公司取得成功,产品得到了下游用户认可。独石化优化产品结构工作取得重要突破。 今年年初以来,独石化通过市场研判,针对重包装膜用于包装塑料原料、化肥等产品的巨大需求,开始进行产品升级改进攻关工作。 虽然目前国内大多使用PP编织袋和纸袋作为重包装袋,但重包装膜以其具有的高性能和高包装效率正受到越来越多的关注,特别是随着国内数个石化大项目的陆续开工,使重包装膜在我国的前景极为看好。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |