牌号简介 About |
---|
350微米粉末中的增强流动性聚醚酰亚胺(TG 217C)。生态符合 Enhanced flow Polyetherimide (Tg 217C) in 350 micron powder. ECO Conforming. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
密度 Density |
1.27 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
337℃,6.60kg 337℃,6.60kg |
18 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
340℃,5 kg 340℃,5 kg |
13.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 to 0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
23℃ 23℃ 8 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 9 |
ISO 180/1A | ||
-30℃ -30℃ |
ISO 180/1A | ||
23℃ 23℃ |
ISO 180/1A | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 11 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
75℃ 75℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-20~150℃ MD:-20~150℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在空气中 1.6 mm in air |
kV/mm | ASTM D149 | |
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
2.45 GHz 2.45 GHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/5 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 7 |
|||
屈服,100 mm跨度 Yield, 100 mm span 7 |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 0.10 in/min |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
中国聚氨酯市场会向印度市场转移吗?
2016-10-18 据悉,亚太地区聚氨酯市场已经成为促进区域产业需求的中坚力量,而在背后主导的,是中国和印度。中国是龙头老大,印度是个中翘楚。印度的聚氨酯市场仅有中国的1/10左右,中印这两大市场未来将有什么的走向呢? 印度有汽车、电子和家居三个需求大户。汽车业占全国总收入的25%,是印度的支柱产业,近年来一直保持良好的增长趋势。电子行业则有望给聚氨酯市场带来可观的利润,随着人们开始意识到对电路和传感器等电子元件封装的重要性,不断刺激着电子行业对聚氨酯的需求。印度地区国民可支配收入的增长以及生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |