牌号简介 About |
---|
HP53-25-155是一种高性能高密度聚乙烯共聚物,用于要求优异的环境应力抗裂性(ESCR)的吹塑应用。本产品符合美国食品药品监督管理局21CFR 177.1520的要求。 HP53-25-155 is a high performance high density polyethylene copolymer for use in blow molding applications requiring excellent environmental stress crack resistance (ESCR). This product meets the Food and Drug Administration requirements of 21CFR 177.1520. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ASTM D4883 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.22 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
200 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
68 | ASTM D2240 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
27.6 | MPa | ASTM D638 |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790A | ||
2% 正割 2% secant |
MPa | ASTM D790-A | |
正切 tangent |
MPa | ASTM D790-A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
Area Area |
kJ/m² | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
全国政协委员刘红光:引导公众正确认识化工
2022-03-12 今年全国两会期间,出席全国政协十三届五次会议的全国政协委员、中海油天津化工研究设计院首席顾问刘红光在接受记者采访时表示,目前社会上对化工存在不少误解,在今年的全国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |