牌号简介 About |
---|
LTP PO-8100系列材料,是以聚烯烃为基材、聚苯硫醚(PPS)树脂为成核剂,填充改性增强的高性能复合材料,主要应用于机械零部件。取代PA6、PA66、PET、PBT系列阻燃材料。可在其热变形温度低20℃下长期使用。
LTP PO-8100系列材料具有优良耐酸碱性、阻燃性、耐候性及机械力学强度。 LTP 8100 serials is reinforced composite materials with high performance based on polyolefin and PPS, and are extensively applied in injection mold to structure and parts of machine, electric appliance and automobiles. It is used to replace materials of PA PBT (PET), PPO (PPE), and PC/ABS serial. The LTP 8100 serials materials have the characteristics of high impact strength, high dimensional stability and low moisture absorption. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate 2 |
|||
TD:3.0 mm TD:3.0 mm |
0.80 | % | |
MD:3.0 mm MD:3.0 mm |
0.50 | % | |
吸水率 Water absorption rate |
|||
饱和 saturated |
0.10 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
80.0 | MPa | GB/T 1040 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | GB/T 1040 | |
弯曲强度 bending strength |
MPa | GB/T 1042 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | GB/T 1043 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
℃ | GB/T 1634 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | GB/T 1410 | |
体积电阻率 Volume resistivity |
ohms·cm | GB/T 1410 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
GB/T 1409 | ||
25 ℃,1 kHz 25 ℃,1 kHz |
GB/T 1409 | ||
25 ℃,1 MHz 25 ℃,1 MHz |
GB/T 1409 | ||
耗散因数 Dissipation factor |
GB/T 1409 | ||
25℃,1 kHz 25℃,1 kHz |
GB/T 1409 | ||
25℃,1 MHz 25℃,1 MHz |
GB/T 1409 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 80x80x3 mm |
【新闻资讯】查看全部
继杜邦陶氏并购后 新一轮并购案浮出水面
2016-02-25 去年两大化工巨头杜邦和陶氏化学合并成为了年度大新闻,近日重组案有了新进展。今日,“陶氏杜邦公司” 公布了意向拆分为三家独立上市公司后农业公司在美国的营运地点安排。至此,计划中的三家独立上市公司都明确了细节。 陶氏化学董事长兼首席执行官利伟诚(Andrew N. Liveris)表示,“陶氏化学与杜邦公司计划进行的农业业务合并将打造一家总部设在美国的全球领先企业,其业务规模和广度将能为世界范围内的农作物种植业者提供更优的价值与更多的选择,并抗衡全球最大的竞争对手。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |