牌号简介 About |
---|
Nucrel® 960是乙烯和甲基丙烯酸的共聚物,通常由15 wt%的甲基丙烯酸制成。它固有的柔韧性,不需要增塑剂。该树脂可以着色,紫外线稳定的外部应用和油漆或电镀的特殊装饰效果。 Nucrel® 960 is a copolymer of ethylene and methacrylic acid, made with nominally 15 wt% methacrylic acid. It is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for exterior applications and painted or plated for special decorative effects. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ASTM D792 |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
60 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
60 | g/10min | ISO 1133 |
甲基丙烯酸含量 Methacrylic acid content |
15.0 | wt% | |
Methacrylic Acid Content Methacrylic Acid Content |
wt% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
冰点 freezing point |
|||
-- -- |
℃ | ISO 3146 | |
-- -- |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
理化所发现苯乙烯在催化下可以与脂肪族醇和酮类反响
2016-03-08 中科院理化所王乃兴研究员课题组发现苯乙烯在催化条件下能够与脂肪族醇和酮类直接发生区域选择性反应,一步合成得到有用的双官能团化复杂产物。 绝大多数有机化合物含有C-H键,对不活泼C-H键进行催化官能化在有机合成化学中意义重大。最近,王乃兴课题组发现了芳基烯烃与脂肪族醇的氧化偶联新反应。在氯化锰和叔丁基过氧化氢的催化下,苯乙烯经与脂肪醇的α-C(sp3)-H键官能团化,一步得到目标产物。经过拓展,发现芳基烯烃与低沸点脂肪族醇都能以中等以上的收率很好地发生该反应。所得到的21个目 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |