牌号简介 About |
---|
SABIC® LLDPE 318BJ是一种丁烯线性低密度聚乙烯树脂,通常设计用于易于加工,并专门配制用于铸膜挤出高温下的最佳热稳定性。SABIC® LLDPE 318BJ铸膜具有优异的光学性能、抗穿刺性和撕裂强度。SABIC® LLDPE 318BJ不含TNPP。SABIC® LLDPE 318BJ是一种丁烯线性低密度聚乙烯天然树脂,通常用于电线和电缆应用。SABIC® LLDPE 318BJ含有高水平的抗氧化剂,不含任何抗阻剂和/或抗滑剂。具有良好的抗环境应力开裂性能。SABIC® LLDPE 318BJ通常用作绝缘和护套应用的基树脂。应用铸膜:SABIC® LLDPE 318BJ树脂通常用于手和托盘拉伸包装。电线电缆:电信和电力电缆(低压、中压、高压)护套。无卤阻燃(HFFR)化合物。一步或两步硅烷交联电缆绝缘。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 318BJ is a butene linear low density polyethylene resin typically designed for easy processing and specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast film produced from SABIC® LLDPE 318BJ exhibit excellent optical properties, puncture resistance and tear strength. SABIC® LLDPE 318BJ is TNPP free. SABIC® LLDPE 318BJ is a butene Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 318BJ contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It exhibits good Environmental Stress Crack Resistance (ESCR). SABIC® LLDPE 318BJ is typically used as base resin for insulation and jacketing applications. Application Cast Film: SABIC® LLDPE 318BJ resin is typcially used for hand and pallet stretch wrap. Wire & Cable: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.8 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
52 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
2.00 | J | ASTM D5748 |
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
撕裂强度 tear strength 3 |
|||
TD,20 µm TD,20 µm 3 |
kN/m | ISO 6383-2 | |
|
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
|||
1% 正割 1% secant |
MPa | ASTM D790 |
备注 |
---|
2. 2000 V/sec |
3. Cast Film |
【新闻资讯】查看全部
10家!湖南公示第一批化工园区认定名单
2021-04-15 搜料网资讯: 4月12日,湖南省发展和改革委员会网站公示了湖南省第一批化工园区认定评估建议名单,共有10家园区上榜。 进入名单的园区分别是:湖南岳阳绿色化工产业园、洪江高新 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |