牌号简介 About |
---|
滑动改性双向拉伸聚丙烯薄膜非热封双面处理 Slip Modified BIAXIALLY ORIENTED POLYPROPYLENE FILM NON-HEAT SEALABLE, TWO SIDE TREATED |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability 2 |
|||
TD,130℃ TD,130℃ |
< 3.0 | % | |
MD,130℃ MD,130℃ |
< 5.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
动态 dynamic |
0.20 | ASTM D1894 | |
静态 static state |
0.25 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
MPa | ASTM D882 | |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
水气透过率 Water vapor transmittance |
|||
38℃,90% RH 38℃,90% RH |
g/m²/24 hr | ASTM F1249 | |
用量 dosage 3 |
m²/kg | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面能 Surface energy |
ASTM D2578 | ||
-- -- 4 |
dyne/cm | ASTM D2578 | |
-- -- 5 |
dyne/cm | ASTM D2578 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 5 minutes |
3 Internal Method |
4 Corona Side |
5 High Energy Flame Side |
【新闻资讯】查看全部
吉兰泰盐化20万吨糊状PVC项目开建
2016-05-05 日前,规划建设年产20万吨糊状PVC生产装置项目在阿拉善经济开发区开工建设。 该项目由中盐吉兰泰盐化集团有限公司投资建设,总投资20亿元。项目采用国内领先的微悬浮法生产糊状PVC,可生产多种牌号的产品,破解了当前中盐吉盐化集团只能生产SG-5型通用型聚氯乙烯(PVC)树脂的难题,有利于企业长远发展。据了解,中盐吉兰泰盐化集团公司是我区的大型骨干企业和盐化工国有龙头企业。近年来,该公司依托阿拉善盟丰富的盐煤等优势,致力于发展盐化工循环产业,先后开工建设了40万吨/年聚氯乙烯生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |