牌号简介 About |
---|
AMC©8590是一种具有韧性乙烯基酯基体的短切碳纤维增强片状模塑料(SMC)。它很容易成型,提供高强度、抗疲劳、高耐热性和低密度的零件。碳纤维是聚丙烯腈基12K丝束。 AMC© 8590 is a chopped carbon fiber reinforced sheet molding compound (SMC) in a toughness vinyl ester matrix. It is easily moldable and provides parts that are high strength, fatigue resistant, with high heat resistance and a low density. The carbon fiber is PAN based 12K tow. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.48 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.0 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
55200 | MPa | ASTM D638 |
拉伸强度 tensile strength |
283 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
38600 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
玻璃化转变温度 Glass transition temperature |
℃ | ASTM E1356 | |
贮藏期限 Storage period |
|||
24℃ 24℃ |
wk | ||
脱模时间 stripping time |
|||
138℃ 138℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
四个方面剖析注塑成型缺陷银丝成绩
2017-11-27 银纹主要是原料干燥不彻底,由水分或挥发成分造成的(主要有水汽、分解气、溶剂气、空气的干扰)。当产生银丝时,首先要用彻底干燥的颗粒料进行成型实验,若这样尚不能消除,可检查其他原因。 银丝产生的具体原因分述如下: 1、注塑机方面: (1)料筒、螺杆磨损或过胶头、过胶圈存在料流死角,长期受热而分解。 (2)加热系统失控,造成温度过高而分 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |