牌号简介 About |
---|
产品描述:SABIC® LDPE HP2027N是一种低密度聚乙烯级,无滑脱和防堵塞添加剂,密度增加。它通常表现出更好的下拉能力和高输出。薄膜具有优良的光学性能和良好的热封性能,同时具有较高的刚性。典型应用:包装袋、表面保护膜、复合膜、食品包装膜。需要高光学性、高硬度和下测量的胶片。本产品不适用于医疗和制药应用。 PRODUCT DESCRIPTION: SABIC® LDPE HP2027N is a Low Density Polyethylene grade without slip and anti-block additives, with increased density. It typically exhibits better draw down ability with high output. Films typically exhibit excellent optics and good heat seal properties combined with high rigidity. TYPICAL APPLICATIONS: Bags & pouches, surface protection films, lamination films, food packaging films. Films where high optics, enhanced stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.927 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
0.05 mm 0.05 mm |
300 | MPa | ISO 527-2 |
摩擦系数 friction coefficient |
> 80 | % | ISO 8295 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
薄膜厚度 film thickness |
|||
拉伸强度 tensile strength |
ISO 527-3 | ||
屈服,0.05 mm Yield, 0.05 mm |
MPa | ISO 527-2 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
20°,50 µm,吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
60°,50.0 µm,吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美国丙烯库存持续远高于500万桶
2019-01-18 1月16日报道称,美国能源情报署周三公布的数据显示,美国丙烯库存继续远高于500万桶大关,创下7年新高。 截至1月11日当周,美国非燃料用丙烯库存为545.3万桶,较上周增加33.7万桶。 上周的库存水平也代表着五周的增长。自2012年1月6日以来,国内库存量未达到或超过这一水平,当时最高库存量为563.3万桶。 这一增长符合一些市场预期,即到2019年,除非丙烷脱氢生产出现重大问题,否则库存水平将继续增加。 不过,国内丙烯库 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |