牌号简介 About |
---|
Hifax CA 387 A是一种反应器TPO(热塑性聚烯烃),采用Lyondellbasell专有的Catalloy工艺技术制造。它具有高熔体流动性和冲击、刚度、可加工性和可涂装性的良好平衡。Hifax CA 387 A主要用于需要高耐久性的喷漆汽车保险杠蒙皮,以及其他具有喷漆和耐候性要求的注塑件。它还被用作复合材料的一种组分,用于广泛的工业应用。该等级为天然颗粒形式。有关法规遵从性信息,请参阅HIFAX CA387产品管理公告(PSB)。 Hifax CA 387 A is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It has high melt flow and an excellent balance of impact, stiffness, processability and paintability. Hifax CA 387 A is primarily used for painted automotive bumper fascias that require high durability, and for other injection molded parts with paintable and weatherable requirements. It is also utilized as a component in compounded materials for a wide range of industrial applications. The grade is available in natural pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
63 | ISO 868 | |
拉伸强度 tensile strength |
|||
屈服 yield |
18.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus 2 |
|||
弦,23℃ String, 23 ℃ 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃,完全断裂 -40 ℃, completely fractured |
kJ/m² | ISO 180 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 180 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-40℃,3.20 mm,Energy at Peak Load,Ductile Failure -40℃,3.20 mm,Energy at Peak Load,Ductile Failure |
J | ASTM D3763 | |
23℃,3.20 mm,Energy at Peak Load,Ductile Failure 23℃,3.20 mm,Energy at Peak Load,Ductile Failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,079 in/min |
3 7,22 ft/sec |
【新闻资讯】查看全部
受“国门利剑2017”影响 塑料现货端需求疲软
2017-05-24 2017年,塑料期货市场迎来第十个年头。十年里,线型低密度聚乙烯(LLDPE)、聚氯乙烯(PVC)和聚丙烯(PP)期货品种先后登陆期货交易市场,大连塑料期货市场规模不断扩大、产业客户参与积极性日益提高,形成了品种较为完善、功能有效发挥的塑料期货品种体系。由大商所主办的第十届“中国塑料产业大会”于5月24日在杭州黄龙饭店召开。 5月23日下午浙商期货在围绕“聚烯烃产业与全球视角下的塑料行情解析”开展了塑料产业大会同期活动。 大连商品交易所工业品事业部高级经理周 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |